Advanced Materials Enhancing elongation at break Quarter 1, 2014

Table of contents Flexible epoxy building blocks Product selection Elongation at break, modulus and viscosity Tg and water absorption Flexible hardeners Product selection Elongation at break Modulus and glass transition temperature Pot life and time to reach 90% conversion Advanced Materials 2

Flexible epoxy building blocks < Table of content Flexible epoxy building blocks > Flexible hardeners > Product selection Product Reactivity vs. Bis-A epoxy resin at room temperature Impact on mechanical properties vs.Bis-A epoxy resin at room temperature Viscosity (mPa.s) Araldite® DY 3601 Slower 10 times higher elongation 42 - 52 mPa.s Araldite® DY-L Slower 10 times higher elongation 160 - 240 mPa.s Araldite® PY 4122 Slower Very low modulus 25 times higher elongation 700 - 1400 mPa.s Araldite® DY-D Similar Slightly lower modulus 2 times higher elongation 15 - 25 mPa.s Araldite® CY 184 Similar Higher modulus 2-3 times higher elongation 700 - 1000 mPa.s Advanced Materials 3

Flexible epoxy building blocks < Table of content Flexible epoxy building blocks > Flexible hardeners > Elongation at break, modulus and viscosity of the mix Araldite® PY 4122, Araldite® DY-D and Araldite® CY 184 Araldite® epoxy resin + Aradur® 20315 mixed at stoichiometry Cure profile: 1 h at 80°C + 1 h at 120°C + 1 h at 150°C Advanced Materials 4

Flexible epoxy building blocks < Table of content Flexible epoxy building blocks > Flexible hardeners > Tg and water absorption Araldite® PY 4122, Araldite® DY-D and Araldite® CY 184 Araldite® epoxy resin + Aradur® 20315 mixed at stoichiometry Cure profile: 1 h at 80°C + 1 h at 120°C + 1 h at 150°C Advanced Materials 5

Flexible hardeners < Table of content Flexible epoxy building blocks > Flexible hardeners > Product selection Product Latency / reactivity Impact on mechanical properties cured with Bis-A epoxy resin Viscosity (mPa.s) Aradur® 70 Very slow cure at RT Very high flexibility Max elongation 400 % at RT and > 250 % at -10°C 16 000 - 27 000 Aradur® 3275 Good compromise between pot life and curing time at RT High level of flexibility Elongation 110% at RT and up to 50 % down to -10 °C 200 - 300 Aradur® 15-1 Fast cure at RT Flexible Elongation 50% at RT 100 - 300 Aradur® 90 Extremely fast cure at RT Good modulus combined with a 8% elongation at RT 10 000 - 16 000 Advanced Materials 6

Flexible hardeners < Table of content Flexible epoxy building blocks > Flexible hardeners > Elongation at break Aradur® 70, Aradur® 3275, Aradur® 15-1 and Aradur® 90 Araldite® GY 250 (BisA-diglycidyl ether) + hardener mixed at stoichiometry RT cure profile: 2 weeks at 25°C - HT cure profile: 10 h at 80°C Advanced Materials 7

Flexible hardeners < Table of content Flexible epoxy building blocks > Flexible hardeners > Modulus and glass transition temperature Aradur® 70, Aradur® 3275, Aradur® 15-1 and Aradur® 90 Araldite® GY 250 (BisA-diglycidyl ether) + hardener mixed at stoichiometry RT cure profile: 2 weeks at 25°C - HT cure profile: 10 h at 80°C - Tg measured via DMA (Tan delta Peak) Advanced Materials

Flexible hardeners < Table of content Flexible epoxy building blocks > Flexible hardeners > Pot life and time to reach 90% conversion at 60°C and 80°C Aradur® 70, Aradur® 3275, Aradur® 15-1 and Aradur® 90 Araldite® GY 250 (BisA-diglycidyl ether) + hardener mixed at stoichiometry Conversion measured with DSC (isotherm) - Pot life measured with Geltimer (TECAM) on 100 g mix at 25°C Advanced Materials 9

Keep our products at your fingertips View the brochure on SlideShare Download our mobile apps on your smartphone With this brochure get an overview of our comprehensive range of building blocks for formulators. With these apps select immediately the right: !! Araldite® industrial adhesive for your specific need !! Araldite® composite formulated system for your process / application Access the product description or send us an email to request the technical data sheet. Araldite® - Adhesives (Europe) Download on iPhone | Android Huntsman - Composite resins (Europe) Download on iPhone | Android Advanced Materials 10

For more information www.huntsman.com/advanced_materials advanced_materials@huntsman.com Europe Huntsman Advanced Materials (Switzerland) GmbH Klybeckstrasse 200 P.O. Box - 4002 Basel Switzerland Tel. +41 61 299 20 41 Fax +41 61 299 20 40 Advanced Materials 11

Legal Disclaimer Copyright © 2014 Huntsman Corporation or an affiliate thereof. All rights reserved. The use of the symbol ® herein signifies the registration of the associated trademark in one or more, but not all, countries. While the information and recommendations included in this publication are, to the best of Huntsman s knowledge, accurate as of the date of publication, nothing contained herein is to be construed as a representation or warranty of any kind, express or implied.

Add a comment

Related presentations

Related pages

Enhancing elongation at break - Quarter 1, 2015

Enhancing elongation at break Quarter 1, 2015 . ... Elongation at break, modulus and viscosity Tg and water absorption Flexible hardeners Product selection
Read more

www.sciencedirect.com

Most rubber materials are subjected to oxidation. The rate of oxidation depends on the type of rubber, processing method, and end-use conditions. The oxidation
Read more

elongation | physics | Britannica.com

... a material elongates and eventually breaks. ... Retrieved from http://www.britannica.com/science/elongation ... You can also highlight a section ...
Read more

DIN 53504 - Techstreet -Technical Information Superstore

DIN 53504 Testing of ... Highlight Bookmark ... tensile stress at yield, elongation at break and stress values in a tensile test
Read more

Non-covalent functionalization of graphene oxide by pyrene ...

... Young's modulus, elongation at break and toughness of PMMA were increased by 23%, 54%, 117%, and 218%, respectively, ... Highlight your research.
Read more

Enhancing structural properties and antioxidant activity ...

Enhancing structural properties and antioxidant activity of kefiran films by chitosan addition. ... Highlights • Physical ... elongation at break, ...
Read more

Fig. 12. Elongation at break and shore A hardness of MVQ ...

Fig. 12. Elongation at break and shore A hardness of MVQ fi lled with various contents of GNPs. ... Article: Enhancing the thermal, electrical, ...
Read more

Materials Search | Senvol

... if you only want to search for Stratasys materials, ... for titanium materials that have an elongation at break of at ... News Highlights ...
Read more

Enhancing the Mechanical Properties of Cross-Linked Rubber ...

The current study aims to vary and highlight the ... Elongation at Break. ... 3 wt% was found to be the most effective in enhancing the mechanical ...
Read more